| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24hr，in 23℃ | ASTM D-570 | 0.23 | % |
| 熔体流动速率 | 300℃ 1.2kg | ISO 1133(ASTM D-1238) | 19 | g/10min | |
| 物理性能 | 光线透过率 | 3mm厚 | ASTM D-1003 | 85-89 | % |
| 比重 | --- | ASTM D-792 | 1.9 | --- | |
| 泰伯磨耗量 | 1000round | ASTM D-1044 | 12 | mg | |
| 成形收缩率 | --- | ASTM D-955 | 0.5～0.7 | % | |
| 机械性能 | 挠曲强度 | --- | ISO 178(ASTM D-790) | 93(950) | MPa(Kg/cm2) |
| 挠曲弹性率 | --- | ISO 178(ASTM D-790) | 2350(24000) | MPa(Kg/cm2) | |
| IZOD冲击强度 | 4mm with notch 3.2mm with notch | ISO 180(ASTM D-256) | 65(80) | KJ/m2(kg?cm/cm2) | |
| 洛氏硬度 | --- | ISO 2039-2 ASTM D-785 | R120(M75) | --- | |
| 引张降伏强度 | --- | ISO R-527(ASTM D-638) | 64(650) | MPa(Kg/cm2) | |
| 引张破坏强度 | --- | ISO R-527(ASTM D-638) | 68(700) | MPa(Kg/cm2) | |
| 引张弹性率 | --- | ISO R-527(ASTM D-638) | 2300(23500) | MPa(Kg/cm2) | |
| 引张破坏伸率 | --- | ISO R-527(ASTM D-638) | 115 | % | |
| 电气性能 | 绝缘破坏电压 | 1.6mm厚 | --- | 30 | Kv/mm |
| 体积电阻率 | --- | ASTM D-257 | ＜1016 | Ω?cm | |
| 诱电率 | 60Hz(106Hz) | ASTM D-150 | 2.91(2.85) | --- | |
| 诱电正接 | 60Hz(106Hz) | ASTM D-150 | 6.6×10-4(9.2×10-3) | --- | |
| 热 性 能 | 燃烧性 | 1.47mm厚 | UL 94 | V-2 | --- |
| 热变形温度 | 1.8Mpa 18.6kg/cm2 | ISO 75(ASTM D-648) | 128 | ℃ | |
| 维卡软化点 | --- | ISO 306 | 145 | ℃ | |
| 线膨胀系数 | --- | ASTM D-696(ASTM D-695) | 6.5 | 10-5cm/cm/℃ | |
以上为台湾\日本出光PC IR1900塑胶原料物性数据仅供参照，请以实际操作为准！